ASTM A286 SUH 660 Bar Rownd
ASTM A286 SUH 660 bar crwn
ASTM A286 SUH 660 bar crwn
A286 Dur di-staen Cyfansoddiad Cemegol
| Elfen | Cynnwys (%) |
|---|---|
| Haearn, Fe | 54 |
| Nickel, Ni | 25.5 |
| Cromiwm, Cr | 14.8 |
| Titanium, Ti | 2.13 |
| Molybdenum, Mo | 1.30 |
| Manganîs, Mn | 1.0 |
| Silicon, Si | 0.50 |
| Vanadium, V | 0.30 |
| Alwminiwm, Al | 0.18 |
| Carbon, C | 0.040 |
| Ffosfforws, P | 0.020 |
| Sulfur, S | 0.015 |
| Boron, B | 0.0060 |
A286 Dur di-staen Priodweddau Ffisegol
| Eiddo | Metrig | Imperial |
|---|---|---|
| Dwysedd | 7.92 g/cm3 | 0.286 lb/in3 |
| Pwynt toddi | 1399°C | 2550°F |
Dur di-staen gradd 660 Eiddo Mecanyddol
Cryfder Cynnyrch Dur Di-staen A286
| Eiddo | Metrig | Imperial |
|---|---|---|
| Cryfder tynnol | 1035 APC | 150100 psi |
| Cryfder y cynnyrch (@strain 0.200%) | 759 MPa | 110000 psi |
| Elongation yn ystod egwyl | 25% | 25% |
| Lleihau arwynebedd | 40% | 40% |
| Hardness, Brinell (amcangyfrifir o werth Rockwell C ar gyfer prawf Brinell gyda 3000 kg o lwyth/pêl ddieeter 10 mm) | 304 | 304 |
| Hardness, Knoop (amcangyfrifir o werth Rockwell C) | 330 | 330 |
| Caledwch, Rockwell C | 32 | 32 |
| Hardness, Vickers (amcangyfrifir o werth Rockwell C) | 318 | 318 |
Tagiau poblogaidd: astm a286 suh 660 bar crwn, Tsieina, gweithgynhyrchwyr, ffatri, pris, wedi'i addasu